NON ETCHING OXIDE REMOVER
FOR POLISHED STAINLESS STEEL
Quickly removes spot and seam weld oxides WITHOUT ETCHING polished stainless steel.
Works Fast - No abrasives - No grinding - No wire brushing.
Use OX-OUT #155 as received. If needed, remove oil or soil from parts with Chem Clean 101 or solvent prior to dipping.
The correct immersion time limits should be determined by testing. During test, remove parts at frequent intervals to evaluate time of cleaning.
Use at room temperature or warm up to 180 degrees. Dip parts while warm from processing for faster cleaning. Small pieces will take from one to thirty minutes.
Rinse in clean water. Work areas should be ventilated.
|POWER PAK #85
Large pieces which cannot be immersed that have spot or seam weld marks can be ElectroCleaned safely and quickly using POWER PAK #85 and OX-OUT #155.
Attach electrical clip to work piece, turn on the power switch, select power range, dip applicator into OX-OUT #155 and wipe over weld area ... no pressure needed!.
Rinse or wipe with wet sponge and clean water.
Polyethylene, polypropylene, PVC tanks or trays, or stainless steel lined with polyethylene or PVC. Stoneware crocks can be used in water bath to warm OX-OUT #155.
DO NOT USE BREAKABLE GLASS CONTAINERS. STAINLESS STEEL CONTAINERS ALONE WILL REACT WITH #155 AND DELUTE IT'S STRENGTH.|
Strong Acid Mixture ... Personnel handling and using OX-OUT # 155 should wear proper acid proof clothing and gloves. Eye protection is required. Avoid contact with skin, eyes or clothing.
See Material Safety Data Sheet for hazard communication standards.